Makrolon® 8025

Polycarbonate; 20 % glass fiber reinforced; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; milled fiber; high viscosity; easy release; available in opaque colors only

About

Product Types

  • Polycarbonate

Material

Plastics
Dimensionally stable

Typical Values

Rheological properties

Property Test Condition Value Unit Standard
Melt Volume-flow Rate (MVR) 300 °C/ 1.2 kg 6 cm³/10min ISO 1133-1
Melt Mass-flow Rate (MFR) 300 °C/ 1.2 kg 6.5 g/10 min ISO 1133
Molding Shrinkage, parallel 60x60x2 mm/ 500 bar 0.55 % ISO 294-4
Molding Shrinkage, normal 60x60x2 mm/ 500 bar 0.35 % ISO 294-4
Molding Shrinkage, parallel / normal Value range based on general practical experience 0.3 - 0.45 % b.o. ISO 2577

Mechanical properties (23 °C/50 % r. h.)

Property Test Condition Value Unit Standard
Tensile modulus 1 mm/min 4,000 MPa ISO 527-1,-2
Yield Stress 50 mm/min 58 MPa ISO 527-1,-2
Yield Strain 50 mm/min 3.5 % ISO 527-1,-2
Strain at Break 5 mm/min 6.5 % ISO 527-1,-2
Stress at Break 5 mm/min 50 MPa ISO 527-1,-2
Flexural Modulus 2 mm/min 3,700 MPa ISO 178
Flexural Strength 2 mm/min 100 MPa ISO 178
Flexural Strain at Flexural Strength 2 mm/min 5.4 % ISO 178
Flexural Stress at 3.5 % Flexural Strain 2 mm/min 95 MPa ISO 178
Izod Notched Impact Strength 23 °C/ 3 mm 12 kJ/m² ISO 7391/b.o. ISO 180/A
Izod Notched Impact Strength 23 °C/ 3 mm 12 kJ/m²
Charpy Notched Impact Strength 23 °C/ 3 mm 12 kJ/m² ISO 7391/based on ISO 179/1eA
Charpy Notched Impact Strength 23 °C/ 3 mm 12 kJ/m²
Charpy Impact Strength -60 °C 65 kJ/m² ISO 179/1eU
Charpy Impact Strength -30 °C 65 kJ/m² ISO 179/1eU
Charpy Impact Strength 23 °C 55 kJ/m² ISO 179/1eU
Puncture Impact Properties - Maximum Force -30 °C 2,800 N ISO 6603-2
Puncture Impact Properties - Maximum Force 23 °C 3,300 N ISO 6603-2
Puncture Energy -30 °C 10 J ISO 6603-2
Puncture Energy 23 °C 20 J ISO 6603-2
Ball Indentation Hardness 136 N/mm² ISO 2039-1
Tensile Creep Modulus 1000 h 3,500 MPa ISO 899-1
Tensile Creep Modulus 1 h 3,700 MPa ISO 899-1

Thermal properties

Property Test Condition Value Unit Standard
Temperature of Deflection under Load 0.45 MPa 141 °C ISO 75-1,-2
Temperature of Deflection under Load 1.80 MPa 134 °C ISO 75-1,-2
Vicat Softening Temperature 50 N; 120 °C/h 147 °C ISO 306
Vicat Softening Temperature 50 N; 50 °C/h 146 °C ISO 306
Coefficient of Linear Thermal Expansion, parallel 23 to 55 °C 0.45 10⁻⁴/K ISO 11359-1,-2
Coefficient of Linear Thermal Expansion, normal 23 to 55 °C 0.55 10⁻⁴/K ISO 11359-1,-2
Burning Behaviour 6.0 mm V - 1 UL 94
Burning Behaviour 1.5 mm V - 2 UL 94
Burning Rate (US-FMVSS-302) >=1.0 mm PASSED ISO 3795
Oxygen Index Method A 32 % ISO 4589-2
Thermal Conductivity, through-plane 23 °C; 50 % r. h. 0.23 W/(m·K) ISO 8302
Resistance to Heat (Ball Pressure Test) 137 °C IEC 60695-10-2
Relative Temperature Index (Tensile Impact Strength) 1.5 mm 115 °C UL 746B
Relative Temperature Index (Electric Strength) 1.5 mm 125 °C UL 746B
Glow Wire Test (GWFI) 4.0 mm 960 °C IEC 60695-2-12
Glow Wire Test (GWFI) 3.0 mm 960 °C IEC 60695-2-12
Glow Wire Test (GWFI) 2.0 mm 960 °C IEC 60695-2-12
Glow Wire Test (GWFI) 1.5 mm 960 °C IEC 60695-2-12
Glow Wire Test (GWFI) 0.75 mm 800 °C IEC 60695-2-12
Glow Wire Test (GWIT) 3.0 mm 875 °C IEC 60695-2-13
Glow Wire Test (GWIT) 2.0 mm 875 °C IEC 60695-2-13
Glow Wire Test (GWIT) 0.75 mm 850 °C IEC 60695-2-13
Application of Flame from Small Burner Method K and F/ 2.0 mm K1, F1 DIN 53438-1,-3
Needle-flame Test Method F/ 3.0 mm 120 °C IEC 60695-11-5
Needle-flame Test Method F/ 2.0 mm 120 °C IEC 60695-11-5
Needle-flame Test Method F/ 1.5 mm 120 °C IEC 60695-11-5
Needle-flame Test Method K/ 3.0 mm 120 °C IEC 60695-11-5
Needle-flame Test Method K/ 2.0 mm 60 °C IEC 60695-11-5
Needle-flame Test Method K/ 1.5 mm 60 °C IEC 60695-11-5
Flash-Ignition Temperature 470 °C ASTM D1929
Self-Ignition Temperature 550 °C ASTM D1929

Electrical properties (23 °C/50 % r. h.)

Property Test Condition Value Unit Standard
Relative Permittivity 1 MHz 3.3 IEC 60250
Relative Permittivity 100 Hz 3.3 IEC 60250
Dielectric Dissipation Factor 1 MHz 90 10⁻⁴ IEC 60250
Dielectric Dissipation Factor 100 Hz 10 10⁻⁴ IEC 60250
Volume Resistivity 1.00E+14 Ω·m IEC 60093
Surface Resistivity 1.00E+16 Ω IEC 60093
Electric Strength 1 mm 36 kV/mm IEC 60243-1
Comparative Tracking Index (CTI) Solution A 175 IEC 60112
Comparative Tracking Index (CTI M) Solution B 125 IEC 60112
Electrolytic Corrosion A1 IEC 60426

Other properties (23 °C)

Property Test Condition Value Unit Standard
Water Absorption (Saturation Value) Water at 23 °C 0.24 % ISO 62
Water Absorption (Equilibrium Value) 23 °C; 50 % r. h. 0.1 % ISO 62
Density 1,340 kg/m³ ISO 1183-1
Bulk Density Pellets 690 g/cm³ ISO 60
Glass Fiber Content Method A 20 % b.o. ISO 3451-1

Processing conditions for test specimens

Property Test Condition Value Unit Standard
Injection Molding - Melt Temperature 300 °C ISO 294
Injection Molding - Mold Temperature 110 °C ISO 294
Injection Molding - Injection Velocity 200 mm/s ISO 294

Recommended processing and drying conditions

Property Test Condition Value Unit Standard
Standard Melt Temperature 300 °C
Barrel Temperatures Nozzle 290 - 300 °C
Barrel Temperatures Front 280 - 290 °C
Barrel Temperatures Middle 270 - 280 °C
Barrel Temperatures Rear 250 - 260 °C
Mold Temperatures 80 - 120 °C
Hold Pressure (% of Injection Pressure) 50 - 75 %
Plastic Back Pressure (specific) 50 - 150 bar
Peripheral Screw Speed 0.05 - 0.2 m/s
Shot-to-Cylinder Size 30 - 70 %
Dry Air Drying Temperature 120 °C
Dry Air Drying Time 2 - 3 h
Moisture Content max. (%) ≤ 0.02 %
Vent Depth 0.025 - 0.075 mm

 